Effect of Y co-doping on the photoluminescence and lifetime of Er3+ in silicate glasses
Author(s) -
Miao Zhuang,
Shanfeng Li,
Qingyu Zhang
Publication year - 2006
Publication title -
wuli xuebao
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.199
H-Index - 47
ISSN - 1000-3290
DOI - 10.7498/aps.55.4321
Subject(s) - photoluminescence , materials science , doping , absorption (acoustics) , silicate , analytical chemistry (journal) , excited state , absorption spectroscopy , silicate glass , optics , optoelectronics , atomic physics , chemistry , physics , composite material , organic chemistry , chromatography
0.5at% and 1.0at% Er/Y co-doped silicate glasses with different Y2O3 concen trations were fabricated by means of high-temperature solid-state reaction, with the Y concentration varying from 0.0at%—2.5at% and 0.0at%—5.0at%, respectively. By measuring the absorption spectra, the photoluminescence (PL) and PL decay, we studied the dependence of absorption and emission cross-section at 1530nm and the lifetime and PL features on Y concentration. The results showed that Y co-doping enabled the absorption peak to widen and enhanced the absorption. The lifetime was prolonged considerably, especially for the highly Er-doped silicate glasses. However, considerable enhancement of PL intensity was not detected when the glasses were excited by a 980nm laser.