Open AccessSynthesis of TiO2 and ZrO2/TiO2 Composite Microspheres and Their Photo‐Catalytic Degradation of Methylene Blue
Author(s) -
Ali İmran Vai̇zoğullar,
Ahmet Yavuz Balcı,
Mehmet Uğurlu,
M. Hamdi Karaoğlu
Publication year - 2016
Publication title -
afyon kocatepe üniversitesi fen ve mühendislik bilimleri dergisi/fen ve mühendislik bilimleri dergisi
Language(s) - English
Resource type - Journals
eISSN - 2149-3367
pISSN - 2147-5296
DOI - 10.5578/fmbd.25229
Subject(s) - scanning electron microscope , materials science , methylene blue , fourier transform infrared spectroscopy , catalysis , nuclear chemistry , composite number , transmission electron microscopy , photocatalysis , chemical engineering , sol gel , nanotechnology , chemistry , composite material , organic chemistry , engineering
TiO2 and ZrO2/TiO2 composite microsphere particles were synthesized using the sol‐gel\udmethod. Photoactivity of TiO2 and ZrO2/TiO2 were compared. Particles were characterized\udusing X‐ray diffraction (XRD), infrared spectroscopy (FTIR), scanning electron microscopy\ud(SEM) of X‐ray (EDAX), and transmission electron microscopy (TEM). The study revealed that\udTiO2 particles were microspheres. The decorating of ZrO2 particles on TiO2 surface was\udsuccessfully carried out that was proved by SEM and TEM analyzes. The photo‐catalytic\udactivity of TiO2 and ZrO2/TiO2 composite microsphere particles was examined using\udmethylene blue (MB) as reference material under UV lamp. Our findings showed that\udZrO2/TiO2 was more active than TiO2. These findings suggest a new TiO2‐based catalyst\udstructure to synthesize and to emphasize the importance of the shape of the catalyst.TiO2 ve ZrO2/TiO2 kompozit mikroküre partiküllerisol jel yöntemi ile sentezlendi. TiO2 ve ZrO2/TiO2\udpartiküllerinin fotokatalitik aktiviteleri karşılaştırıldı. Partiküller XRD, FTIR, TEM, SEM analiz\udteknikleri ile karakterize edildi. Elde edilen SEM ve TEM bulguları TiO2 partiküllerinin küresel ve\udZrO2 nin TiO2 üzerinde dekore edildiğini gösterdi. Fotokatalitik aktiviteleri Metilen Mavisi\udkullanılarak incelendi. Elde ettiğimiz bulgular ZrO2/TiO2 partiküllerinin TiO2 den daha aktif\udolduğunu göstedi. Yukarıdaki bulgular TiO2 bazlı yeni bir materyalin yapısının sentezini ve\udfotoaktivitede katalizörün yapısal şeklinin önemini vurgulamaktadır