ЦЕМЕНТИЙН ГИДРАТЖИЛТЫН БҮТЭЭГДЭХҮҮНД НАНОЦАХИУРЫН ОКСИД НЭМЭЛТИЙН ҮЗҮҮЛЭХ НӨЛӨӨ

Author(s) -

Д Баатарцэрэн,

Н Жавхлантөгс,

Б Цэрэнханд

Publication year - 2017

Publication title -

proceedings of the mongolian academy of sciences

Language(s) - English

Resource type - Journals

eISSN - 2312-2994

pISSN - 2310-4716

DOI - 10.5564/pmas.v57i2.847

Subject(s) - calcium hydroxide , dissolution , calcium , calcium oxide , hydrate , compressive strength , cement , calcium silicate hydrate , materials science , chemistry , chemical engineering , nuclear chemistry , mineralogy , metallurgy , composite material , organic chemistry , engineering

Addition of nano-silica effected to increase the content of calcium hydrasilicate and to decrease the content of calcium oxide for resulting the hydrate cement. Additional mass percent of nanosilica in all three cements of 1.0 % was important to increase compressive strength because the formation of calcium hydrasilicate is increased and the content of calcium oxide is decreased which were become from the results of X-ray diffraction analysis. Therefore, the addition of nanosilica of 1.0 % is optimal dosage. This is related to the dissolution of calcium hydroxide