Open AccessEffect of Silica Fume as Partial Replacement of Cement on Compressive Strength of Roller Compacting Concrete
Author(s) -
Israr Ahmed,
Aneel Kumar,
Samar Hussain Rizvi,
Mohsin Ali,
Sabir Ali
Publication year - 2020
Publication title -
quaid-e-awam university research journal of engineering science and technology
Language(s) - English
Resource type - Journals
eISSN - 2523-0379
pISSN - 1605-8607
DOI - 10.52584/qrj.1802.21
Subject(s) - silica fume , cement , compressive strength , slump , curing (chemistry) , materials science , composite material , waste management , engineering
Silica fume is an industrial by-product that can be used as a partial replacement of cement to enhance the strength related properties of roller compacting concrete. In past, industrial wastes were used to dump on earth, river, and sea that creates a hazardous environment for aquatic life as well as for humans. Nowadays, the use of industrial by-products as cement replacement is popular in the construction industry because it protects the environment from hazards. In this research, the effect of silica fume as partial replacement of sulphate resisting cement is investigated on the compressive strength of roller compacting concrete. Total four types of mix proportions were casted using concert mix ratio as 1:2:4 to investigate the compressive strength of roller compacting concrete at 7 and 28 days of curing age. The sulphate resisting cement was partially replaced with silica fume by 0%, 5%, 10%, and 15% by weight of cement. The zero slump was maintained in all mixes. It was observed that the mix proportions containing 5% and 15% silica fume replacement showed maximum and minimum compressive strength of roller compacting concrete respectively.