Open AccessPROPERTIES OF TUBES FROM Zr-1% Nb ALLOY AFTER THERMOCHEMICAL TREATMENT AND HYDROGENATION
Author(s) -
V. S. Trush,
V.N. Voyevodin,
П. И. Стоев,
V. М. Fedirko,
A. G. Luk’yanenko,
М.А. Tikhonovsky,
V. А. Panov
Publication year - 2021
Publication title -
problems of atomic science and technology
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.216
H-Index - 17
eISSN - 1562-6016
pISSN - 1682-9344
DOI - 10.46813/2021-135-084
Subject(s) - alloy , materials science , zirconium , zirconium alloy , hydrogen , saturation (graph theory) , diffusion , metallurgy , nitrogen , composite material , thermodynamics , chemistry , organic chemistry , physics , mathematics , combinatorics
The influence of treatment in controlled gas environments with subsequent hydrogenation on the physical and mechanical characteristics of the Zr-1% Nb zirconium alloy has been investigated. The surface hardness and the size of the diffusion-hardened layer of the ring-samples cut from fuel tubes from the Zr-1% Nb alloy after treatment in oxygen- and nitrogen-containing gaseous media with subsequent saturation with hydrogen have been established. The influence of the parameters of the gaseous medium and the modes of thermochemical treatment (TCT) of specimens-rings on the destructive stresses under static load at temperatures of 20 and 380 °C is shown. It was revealed that treatment in the investigated gas environment increases the resistance to hydrogen saturation and has a positive effect on the long-term strength of ring specimens from the zirconium alloy Zr-1% Nb.
Accelerating Research
Robert Robinson Avenue,
Oxford Science Park, Oxford
OX4 4GP, United Kingdom
Address
John Eccles HouseRobert Robinson Avenue,
Oxford Science Park, Oxford
OX4 4GP, United Kingdom