Open AccessSusceptibilidad a grietas inducidas por hidrógeno en ambiente corrosivo de H<sub>2</sub>S de juntas soldadas de acero API 5L-X80
Author(s) -
J. Hilton,
Hipólito Carvajal Fals,
R.E. Trevisan
Publication year - 2009
Publication title -
revista de metalurgia
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.195
H-Index - 18
eISSN - 1988-4222
pISSN - 0034-8570
DOI - 10.3989/revmetalm.0818
Subject(s) - chemistry , microbiology and biotechnology , physics , materials science , nuclear chemistry , biology
The susceptibility to hydrogen-induced cracking in H2S environment of welded API X80 steel was studied. The flux cored arc welding (FCAW) process was employed with E71-T1 and E71-T8K6 wires. The welding parameters were kept constant, but the samples were welded using different preheat temperatures (room temperature and 100°C). The gapped bead-on-plate (G-BOP) test was used. The specimens of modified G-BOP tests were exposed to an environment saturated in H2S, as recommended by the NACE TM0284 standard. The weld beads were characterized by optical microscopy and the level of residual hydrogen in the samples was measured. The fracture surface areas of hydrogen-induced cracking were calculated and the fracture mode was discussed. It was found that the preheating temperature of 100°C was enough to avoid cracking, even in the presence of H2S. It was also found that the E71-T8K6 wire was more susceptible to cracking, and the typical mixed-mode fracture was predominant in all samples