Sodium silicate solutions from dissolution of glasswastes. Statistical analysis

[EN]It has studied the solubility process of four different waste glasses (with different particle sizes, <45 μm and>125 μm) in alkaline solutions (NaOH and NaOH/Na2CO3) and water as a reference and under different conditions of solubility (at room temperature, at 80°C and a mechano-chemical process). Have established the optimal conditions of solubility and generation of sodium silicates solutions, and these were: the smaller particle size (<45 μm), with NaOH/Na2CO3 solution and with temperature during 6 hours of stirring time. The statistical analyses of the results give importance to the studied variables and the interactions. Through 29Si NMR MAS it has confirmed the formation after dissolution processes of monomeric silicate, suitable for use as an activator in the preparation of alkaline cements and concretes.[ES]Se ha estudiado el proceso de solubilidad de cuatro diferentes residuos vítreos (con distintas granulometrías, <45 μm y >125 μm) en disoluciones alcalinas de NaOH y NaOH/Na2CO3 y agua como medio de referencia y bajo distintas condiciones de solubilidad (a temperatura ambiente, a 80°C y con un proceso mecano-químico). Se han establecido las condiciones óptimas de solubilidad y generación de disoluciones de silicato sódico, y estas son: menor tamaño de partícula del residuo vítreo (inferior a 45 μm), con la disolución de NaOH/Na2CO3 y tratamiento térmico a 80°C durante 6 horas de agitación. El análisis estadístico realizado a los resultados obtenidos da importancia a las variables estudiadas y a las interacciones de las mismas. A través de 29Si RMN MAS se ha confirmado la formación, tras los procesos de disolución, de un silicato monomérico, apto para su utilización como activador en la preparación de cementos y hormigones alcalinos.Peer reviewe