Open AccessMicrohardness and Fracture Resistance of Radicular Dentin Treated with Different Concentrations of Calcium Hydroxide in Endodontic Regeneration Procedures
Author(s) -
Sara N. Hashem,
Maha Elhousiny
Publication year - 2021
Publication title -
open access macedonian journal of medical sciences
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.288
H-Index - 17
ISSN - 1857-9655
DOI - 10.3889/oamjms.2021.7803
Subject(s) - calcium hydroxide , indentation hardness , dentistry , root canal , medicine , dentin , significant difference , fracture (geology) , nuclear chemistry , calcium , materials science , composite material , chemistry , microstructure
Purpose: to reveal the effect of different concentrations of prepared calcium hydroxide pastes (70%, 50%, and 30%) used in regenerative endodontic on microhardness and fracture resistance of radicular dentin. Material and methods: Different concentrations of calcium hydroxide (Ca(OH)2) were prepared with measured pH, then forty eight single rooted teeth were prepared and randomized into three groups according to Ca(OH)2 paste concentrations (12 samples each) and 12 samples were availed as control group. Group I: root canal contained 30% Ca(OH)2 paste. Group II: root canal contained 50% Ca(OH)2 paste. Group III: root canal contained 70% Ca(OH)2 paste. Samples were stored at 37 0C with 100% humidity for four weeks for subsequent microhardness and fracture resistance tests. Results: There was a statistically significant reduction of microhardness and fracture resistance between test groups and control group (P≤ 0.05), group III showed a significant reduction in both microhardness and fracture resistance compared to group I. However, there was no significant difference in pH between different concentration of Ca(OH)2. Conclusion: Increasing concentration of Ca(OH)2 paste can negatively affect microhardness and fracture resistance of radicular dentin in revascularization procedure.