Open AccessDegradation of Mechanical Properties of Hybrid Reinforcement with Epoxy-Polyester Matrix Under Water Absorption
Author(s) -
M. Swarnalatha,
Gaurav Gupta,
Ajay Kumar Kaviti
Publication year - 2020
Publication title -
international journal of recent technology and engineering
Language(s) - English
Resource type - Journals
ISSN - 2277-3878
DOI - 10.35940/ijrte.e6500.018520
Subject(s) - composite material , materials science , absorption of water , flexural strength , ultimate tensile strength , epoxy , izod impact strength test , composite number , natural fiber , fibre reinforced plastic , polyester resin , reinforcement , polyester
Natural fiberss represent a good renewable and biodegradable alternative the.. most common man-made reinforcement. Among various fibers, natural fibers are used due to their advantages, easy availability, low density, low production cost and better mechanical properties. The aim of this work is to study the degradation of hybrid composites when exposed to moisture condition at room temperature. Hand lay-up method is used to prepare the laminates with the J-G FRP and epoxy matrix. Water absorption test is carried out by immersing the specimen in water tub at room temperature for different time periods. Mechanical properties.. like Tensile strength, Flexural strength, Impact strength and Hardness are evaluated by performing different tests on laminates. The mechanicall properties of water immersed specimen were tested and compared with dry samples as per the ASTM standard. The composites specimens with J-G FRE matrix absorbs less amount of water when compared to polyester specimens. Equilibrium moisture content and water absorption curves were determined. J-G FRE matrix composite was found to have less water absorption and decreased impact strength is 0.19J / mm2, decreased tensile strength is 61.11MPa, decreased flexural strength is 31.29MPa and decreased stiffness is 13HN compared to J-G FRP matrix composite.