Open AccessPhotocatalytic Degradation of Allura Red by Mn-Ni co-doped Nanotitania under Visible Light Irradiation
Author(s) -
Sankara Rao Miditana,
Prof. T. Siva Rao,
Dr. Shaik Abdul Alim,
Imandi Manga Raju
Publication year - 2019
Publication title -
international journal of innovative technology and exploring engineering
Language(s) - English
Resource type - Journals
ISSN - 2278-3075
DOI - 10.35940/ijitee.k2458.1081219
Subject(s) - anatase , photocatalysis , materials science , scanning electron microscope , diffuse reflectance infrared fourier transform , analytical chemistry (journal) , doping , spectroscopy , rutile , nuclear chemistry , fourier transform infrared spectroscopy , catalysis , nanomaterial based catalyst , transmission electron microscopy , visible spectrum , chemical engineering , nanotechnology , nanoparticle , chemistry , environmental chemistry , optoelectronics , biochemistry , physics , quantum mechanics , engineering , composite material
Photocatalyst has been extensive interest because of it’s new innovation to the reduce the contamination in the environment. A straight forward and economical procedure has been employed by sol-gel technique for the co-doping of Mn2+ and Ni2+ into TiO2 . The co-doped and undoped photocatalysts were described by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Energy dispersive X-ray Spectroscopy (EDX), Fourier transform infrared spectroscopy (FT-IR), UV-Visible Diffused Reflectance Spectroscopy (UV Vis-DRS), Transmission electron Microscopy (TEM) and Brunauer-Emmett-Teller (BET). The portrayal results shows that anatase and rutile mixed phase was observed for some co-doped nanocatalysts and the remaining catalysts exhibits anatase phase only. It was observed by FT-IR that the shifting of frequency of Ti-O-Ti in the catalysts was seen due to substitutional doping of Mn and Ni by replace Ti and O, further the photocatalysts shows rough morphology, irregular shape of particle with size (6.5nm) and having high surface area (135.70 m2/g), less band energy (2.7 eV). The photocatalytic action of these materials was assessed by the degradation of Allura red (AR) as a contaminant. The results shows that AR has degraded within 60 minutes at doping concentrations 0.25 Wt% of Mn2+ion and 1.0 Wt% of Ni2+ ion in TiO2 (NMT2) at an optimum reaction parameters pH-4, catalyst dose 0.070g/L and at AR initial dye concentration 0.010g/L.