Open AccessTHE USE OF NANOSCALE ZINC OXIDE IN WOOD-BASED COMPOSITIONS
Author(s) -
S.A. Neminushchaya,
Е. В. Томина,
A. Dmitrenkov
Publication year - 2021
Language(s) - English
Resource type - Conference proceedings
DOI - 10.34220/mmeitsic2021_256-260
Subject(s) - zinc , moisture , materials science , nanoparticle , oxide , wetting , absorption of water , swelling , nuclear chemistry , chemical engineering , composite material , chemistry , metallurgy , nanotechnology , engineering
The aim of this work was to study compositions based on vegetable oil waste and nanoscale zinc oxide particles for processing natural wood. The sol-gel method was used for the synthesis of zinc oxide nanoparticles. The synthesized zinc oxide nanoparticles did not contain impurities and had a shape close to spherical, and their size did not exceed 20 nm. We used freshly prepared suspensions of zinc oxide nanoparticles in used vegetable oil with their content in the amount of 0.1, 0.5 and 1.0 wt. parts per 100 parts of oil. The wood was treated by hot-cold impregnation. The tests were carried out on samples of birch and pine wood of standard sizes. In the modified samples, the wetting angle, moisture and water absorption, as well as their swelling were determined. It is shown that the use of zinc oxide nanoparticles in compositions based on vegetable oil waste can significantly reduce the moisture and water resistance of wood and reduce its swelling. The optimal dosages of the nanopowder introduced into the used vegetable oil and the conditions of impregnation were selected. The compositions used on the basis of vegetable oil waste are characterized by environmental safety, and the resulting wood samples had an improved appearance.