Open AccessIntegrated Reduction of the Self–Reducing Pellets on the Blast Furnace
Author(s) -
A Vaniukov,
D. A. Kovalyov,
Н. Д. Ванюкова,
I Khodyko,
O Bezshkurenko
Publication year - 2020
Publication title -
teoriâ i praktika metallurgii
Language(s) - English
Resource type - Journals
ISSN - 1028-2335
DOI - 10.34185/tpm.2.2020.01
Subject(s) - blast furnace , tube furnace , pellets , argon , crucible (geodemography) , metallurgy , hydrogen , materials science , coke , pelletizing , reducing atmosphere , vacuum furnace , raceway , tuyere , tube (container) , direct reduced iron , hearth , chemistry , composite material , computational chemistry , organic chemistry , lubrication
The objective of the present work is to research a quantitate ratio of degree direct reduction inside of SRP and degreeof indirect reduction outside of SRP on the top of the blast furnace.The reactions of direct and indirect reduction occurring during the heat treatment of self reducing pellets (SRP) have been studied. In this investigation Blast furnace (BF)sludge which contains particles of coke, has been included in the SRP blend as a source of solid reductant and ironbearing oxides.In the SRP as a part ot the blast furnace burden occur the reactions simultaneously: inside of SRP-direct reduction byCsolid; gasification of carbon and indirect reduction by CO; and outside of SRP-indirect reduction of iron bearing oxidesby reducing gas coming from the hearth of blast furnace through the column of charged materials. The experimentalsetup is shown in Fig. 1. It con-sists of a electrical heating furnace, which can be moved up and down. The quartz tubepasses through the furnace. The reaction zone is in the middle of the furnace. Neutral argon atmosphere is created andfor indirect reduction argon changed - on hydrogen. Gases of argon, hydrogen are introduced into the furnace separately. Wire of nickel alloy chromosome joins the scales test. A thermocouple is located in the tube.The crucible of wirechrome-nickel was permeable.Metohd. The experiments was performed continuously from the start temperature (~200˚C) to the experimental temperature (500 ˚C; 700 ˚C; 900 ˚C; 1100 ˚C) in argon free environment. Upon reaching thedesired temperature argon was replaced by hydrogen during 30 minutes. After that the reduced probe of SRP wascooled in argon. Results. The integrated degree of reduction is equal 100%, which includes 98,6 % direct reduction bysolid carbon under temperatures 1100°C. The chemical analysis of the reduced SRP showed the degree of integratedreduction change from 85,79 % (900 °C) to 92,50 % (1000 °C) and 84,6% (1100°C) and metallization 83,30 % (900 °C),89,90 % (1000 °C), 80,75 % (1100 °C).These data correspond to results of degree of reduction SRP depends on temperature