Open AccessA bone replaceable artificial bone substitute: morphological and physiochemical characterizations
Author(s) -
Jong Chul Park,
Dong Wook Han,
Hwal Suh
Publication year - 2000
Publication title -
yonsei medical journal/yonsei medical journal
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.702
H-Index - 63
eISSN - 1976-2437
pISSN - 0513-5796
DOI - 10.3349/ymj.2000.41.4.468
Subject(s) - crystallinity , materials science , scanning electron microscope , porosity , apatite , irradiation , fourier transform infrared spectroscopy , composite material , composite number , compressive strength , chemical engineering , mineralogy , chemistry , physics , nuclear physics , engineering
A composite material consisting of carbonate apatite (CAp) and type I atelocollagen (AtCol) (88/12 in wt/wt%) was designed for use as an artificial bone substitute. CAp was synthesized at 58 degrees C by a solution-precipitation method and then heated at either 980 degrees C or 1,200 degrees C. In this study, type I AtCol was purified from bovine tail skins. A CAp-AtCol mixture was prepared by centirfugation and condensed into composite rods or disks. The scanning electron-microscopic (SEM) characterization indicated that the CAp synthesized at 58 degrees C displayed a crystallinity similar to that of natural bone and had a high porosity (mean pore size: about 3-10 microns in diameter). SEM also revealed that the CAp heated at 980 degrees C was more porous than that sintered at 1,200 degrees C, and the 1,200 degrees C-heated particles were more uniformly encapsulated by the AtCol fibers than the 980 degrees C-heated ones. A Fourier transformed-infrared spectroscopic analysis showed that the bands characteristic of carbonate ions were clearly observed in the 58 degrees C-synthesized CAp. To enhance the intramolecular cross-linking between the collagen molecules, CAp-AtCol composites were irradiated by ultraviolet (UV) ray (wave length 254 nm) for 4 hours or vacuum-dried at 150 degrees C for 2 hours. Compared to the non cross-linked composites, the UV-irradiated or dehydrothermally cross-linked composites showed significantly (p < 0.05) low collagen degradation and swelling ratio. Preliminary mechanical data demonstrated that the compressive strengths of the CAp-AtCol composites were higher than the values reported for bone.