Open AccessEVALUATION ON RESIDUAL MONOMER OF HDDMA MATRIX SYSTEM ON FIDER REINFORCED CONDOSITES (FRC)
Author(s) -
Siti Sunarintyas,
Widowati Siswomihardjo,
Dyah Irnawati,
Jukka Pekka Matinlinna
Publication year - 2014
Publication title -
dentika
Language(s) - English
Resource type - Journals
eISSN - 2615-854X
pISSN - 1693-671X
DOI - 10.32734/dentika.v18i2.2022
Subject(s) - monomer , materials science , matrix (chemical analysis) , acetonitrile , polymer , analytical chemistry (journal) , polymer chemistry , chemistry , composite material , chromatography
Matrix system used bis-GMA was reported hazardously. An alternative monomer such as 1,6-hexanediol dimethacrylate(HDDMA) was under research. The aim of this study was to evaluate residual monomer content of HDDMA basedmatrix compositions on FRCs (fiber-reinforced composites). Three monomers based on bis-GMA (Sigma-Aldrich,USA),methylmethacrylate (MMA, ProSciTech, Australia), HDDMA (Esstech, USA) were used and also camphorquinone (CQ,Esstech, USA), N,N-cyanoethyl methylaniline (CEMA, Esstech, USA), E-glass fibers (StickTech, Finland). The matrixratios (weight %) were 78.4% bis-GMA+19.6% MMA+1.0% CQ+1.0% CEMA (control-group), 78.4% HDDMA+19.6% MMA+1.0% CQ+1.0% CEMA (EXP-1group), and 49.0% HDDMA+49.0% MMA+1.0% CQ+1.0% CEMA(EXP-2group). Samples with fibers embedded in matrix were light-cured then powdered. Powder of 150mg was dilutedin acetonitrile to 10ml. The solution was filtered then injected into HPLC (20µL). Residual monomer content wasevaluated by mobile phase of acetonitrile and water of 7:3, flow rate 1mL/minute. The size of column was C185µ,125mm length, 4mm diameter. UV detection used 275nm. Data were analyzed by ANOVA. The result showed theaverage of residual monomer content (in %) was: 0.02125±0.00018 (control-group), 0.01660±0.00016 (EXP-1group),0.01676±0.00033 (EXP-2group). The ANOVA showed significant difference of monomer content among the groups(p 0.05). In conclusion, a resinmatrix system based on HDDMA–MMA (EXP-1 and EXP-2 groups) revealed significant difference of residualmonomer content to bis-GMA–MMA (control-group) system. The HDDMA-MMA matrix system had less residualmonomer content than bis-GMA-MMA.