Bonded Magnet Permanen Nd2Fe14B dengan Perekat Silicone Rubber dan Karakterisasinya

Abstrak: Bonded magnet permanen dibuat dengan variasi: 95 %wt. Nd2Fe14B dengan 5% SR, 90 %wt. Nd2Fe14B dengan10% SR, 85 %wt. Nd2Fe14B dengan 15% SR, dan 80 %wt. Nd2Fe14B dengan 20% SR. Kedua bahan baku dicampur denganmenggunakan mixer hingga homogen dan berbentuk pasta. Selanjutnya, campuran tersebut dituang ke dalam cetakan dandibiarkan pada suhu ruang selama 4 jam. Sampel yang telah kering dikeluarkan dari cetakan dan dikarakterisasi melaluipengukuran bulk density dan pengukuran kurva histerisis menggunakan BH-curve Permeagraph. Hasil XRD serbuk Nd2Fe14B(NQP-B) yang dianalisis dengan program GSAS diperoleh bahwa serbuk tersebut memiliki komposisi fasa Nd2Fe14B = 78,14%dan fasa Fe = 21,86%. Komposisi silicone rubber (SR) memberikan pengaruh yang signifikan terhadap nilai bulk density dan3sifat magnetiknya. Sampel dengan 5% berat SR memiliki bulk density terbesar yaitu = 4,67 g/cm, sampel dengan 10% sampai3320% berat SR memiliki nilai bulk density yang lebih rendah yaitu masing masing 3,12 g/cm sampai 3,72 g/cm. Hasil darikurva histerisis BH-curve menunjukkan bahwa semakin banyak persentase SR maka sifat magnetiknya cenderung menurun.Nilai remanansi tertinggi (Br ) adalah = 4,85 kG pada sampel dengan 5% berat SR, tetapi sampel dengan 20% berat SR memilikinilai Br terendah yaitu 2,47 kG.Kata Kunci: magnet permanen, Nd2Fe14B, silicone rubber, BH-curveAbstract: Bonded permanent magnet has been made by using composition: 95 wt.% Nd2Fe14B with 5% SR, 90 wt.% Nd2Fe14Bwith 10% SR, 85 wt.% Nd2Fe14B with 15% SR, and 80 wt.% Nd2Fe14B with 20% SR. Both raw materials were mixed untilhomogen and formed a pasta. Then the pasta was casted to mould and dried at room temperature for 4 hours. The driedsamples were released from the mould and continued with characterization for measurement of bulk density and measurementof hysteresis by using BH-curve permeagraph. The XRD result of Nd2Fe14B (NQP-B) shows that the powder of Nd2Fe14B(NQP-B) contains phases : Nd2Fe14B = 78.14% and Fe = 21.86%. The composition of silicone rubber (SR) influences3siqnificantly to bulk density and magnetic properties. Sample with 5 % of SR has highest bulk density (4.67 g/cm), sample33with 10 % to 20 % of SR have lowest bulk density value, respectively: 3.12 g/cm and 3.72 g/cm. The results of measurementof hysteresis curve found that the amount of SR is more higher so the magnetic properties decline. The highest value ofremanence is 4.85 kG at samples with 5 wt.% of SR, but sample with 20 wt.% of SR has lowest value of remanence (2.47 kG).Keywords: permanent magnet, Nd2Fe14B, silicone rubber, BH-curve