Open AccessAnalysis of the crystallogeometry of tetragonal martensite in indium-cadmium alloys by the method of electron back scattering diffractions
Author(s) -
В. М. Счастливцев,
Yu. V. Khlebnikova,
Д. П. Родионов,
L. Yu. Egorova
Publication year - 2019
Publication title -
doklady akademii nauk. rossijskaâ akademiâ nauk
Language(s) - English
Resource type - Journals
ISSN - 0869-5652
DOI - 10.31857/s0869-5652486144-48
Subject(s) - crystal twinning , martensite , tetragonal crystal system , materials science , indium , alloy , diffusionless transformation , crystallography , scattering , lamella (surface anatomy) , condensed matter physics , metallurgy , composite material , optics , crystal structure , chemistry , microstructure , physics
It was shown in the work using electron back scattering diffractions analysis that when cooling lower than temperature of the martensitic fcc-hct transformation in the alloy In - 4.5 wt% Cd a packet structure is formed consisting of colonies of tetragonal lamella plates. At the next packages there are always three grades of the plates of a tetragonal martensite which are in twinning situation and differing with the direction of the tetragonality axis. Each martensitic plate consists in turn of a set of more shallow submicrotwinning plates alternating in the direction of an axis of tetragonality. On the basis of the obtained data it is possible to conclude that the structure of the package consisting of twinning plates and the structure of the separate martensitic plate consisting, in turn, of submicro-twins submits to the general regularities. At each structural level in group of the neighboring areas the building blocks of three grades differing with the direction of a tetragonality axis are found.