Open AccessADHESION STRENGTH INVESTIGATION OF FILM ANTIFRICTION COATINGS
Author(s) -
Aleksei Yur’evich Rodichev,
Aleksey Rodichev,
А. В. Горин,
А. В. Горин,
Мария Токмакова,
Mariya Tokmakova,
Алексей Киричек,
Andrey Kirichek
Publication year - 2019
Publication title -
vestnik brânskogo gosudarstvennogo tehničeskogo universiteta
Language(s) - English
Resource type - Journals
ISSN - 1999-8775
DOI - 10.30987/article_5db95e857a4e02.22596904
Subject(s) - materials science , coating , adhesion , composite material , elongation , tension (geology) , ultimate tensile strength
The paper is dedicated to the investigation of adhesion strength in film coatings. The goal of the work is a qualitative estimate of the strength of film antifriction coatings applied on friction units of machines. The topicality is grounded by the fact that the friction decrease on surfaces in units ensures the increase of life, power effectiveness and reliability of machinery.
Most of the works are dedicated to the study of manufacturing films, their phase composition, structure, stress-strain properties, whereas in the material offered the adhesion properties of film antifriction coating are emphasized, which is a sufficient novelty.
During the investigations of the adhesion strength of antifriction film coatings there was used a method of a normal detachment. To carry out comparative tests there were prepared four groups of different antifriction coatings. For each coating under testing there were prepared five samples which were loaded with the smooth increase of a breaking tension.
Therefore there are obtained experimental dependences of normal stresses (σ) upon relative elongation (ε), which allow using values obtained for surfaces coated with antifriction film coatings with different areas. Upon completion of coating tests both parts of the samples tested were subjected to visual analysis. In the course of the analysis a character of destruction was defined. As a result of the theoretical and experimental investigations carried out there were drawn conclusions describing a qualitative and quantitative estimate of the adhesion strength of antifriction film coating.