Open AccessPengaruh Variasi Temperatur Quenching pada Aluminium Paduan AlMgSi-Fe12% terhadap Keausan
Author(s) -
Wardoyo Wardoyo,
Sumpena Sumpena
Publication year - 2018
Publication title -
jurnal engine : energi, manufaktur, dan material
Language(s) - English
Resource type - Journals
ISSN - 2579-7433
DOI - 10.30588/jeemm.v2i1.528
Subject(s) - metallurgy , materials science , nuclear chemistry , analytical chemistry (journal) , chemistry , physics , chromatography
The purpose of this research is to determine the effect of heat treatment hardening of Al Mg Si - Fe12% casting aluminium alloys on wear. The tests were carried out on specimens of raw materials and heat-treated specimens with variations of temperature used were 550 o C, 575 o C, 600 o C, and 625 o C, and used 15 minutes of holding time in each heat treatment, then quenching in SAE 20 oil. The method used for wear-tested was high speed ogoshi universal testing machine wear. The result had shown on raw material a specific wear rate was 2.256102E-07 mm 2 /kg. Test results on the specimens that have received heat treatment hardening temperature 550 o C increased the wear value decreased to 1.7471E-07 mm 2 /kg. In materials with temperature heat treatment, 575 o C causes wear values were increased when compared with raw material, respectively, 2,83739E-07 mm 2 /kg. In materials with temperature heat treatment 600 o C also causes wear values were increased when compared with raw material, respectively, 2,65105E-07 mm 2 /kg. Test results on the test material that ha s received heat treatment temperature 625 o C increased the wear value decreased to 2.16777E-07 mm 2 /kg.