Open AccessEvaluation of physical and dynamic mechanical properties of coconut husk ash (CHA) reinforced polyester composites
Author(s) -
Tertsegha Daniel Ipilakyaa
Publication year - 2021
Publication title -
journal of mechanical and energy engineering
Language(s) - English
Resource type - Journals
eISSN - 2544-1671
pISSN - 2544-0780
DOI - 10.30464/jmee.2020.4.4.315
Subject(s) - materials science , composite material , distilled water , composite number , dynamic mechanical analysis , polyester , young's modulus , reinforcement , sieve (category theory) , polymer , chemistry , chromatography , mathematics , combinatorics
The evaluation of physical and dynamic mechanical analysis (DMA) properties was carried out using developed CHA Reinforced Polymer Composite. Sieve analysis of pretreated CHA was done to obtain 75 µm, 150 µm and 300 µm particles sizes. These particles were used at varying compositions of 5%, 10%, 15%, 20% and 25% as reinforcements for polyester composites. The catalyst and accelerator used were Methyl Ethyl Ketone Peroxide and Cobalt Naphthenate respectively. The densities of the evaluated composites made with 150 μm particles were found to be less dense with values ranging from 0.9792 g/cm3 to 1.2561 g/cm3 than those made with 75μm and 300μm. The results also show that the percentage water absorbed by samples increased, ranging from 0 to over 2000 E’/MPa for all percentage reinforcements of CHA, with an increase in the duration of immersion of the samples in distilled water. However, 25% reinforcement had better results for all particle sizes. There were obvious variations of storage modulus, loss modulus and mechanical loss factor with percentage weight of reinforcement, temperature and frequency. The composite with 15 % reinforcement displayed better results and can be used as a material for interior components in aerospace and automobile industries.