Pengaruh Perlakuan Shot Peening Terhadap Korosi Retak Tegang Baja Karbon Rendah Pada Lingkungan Korosif
Author(s) -
Sujita Sujita
Publication year - 2011
Publication title -
dinamika teknik mesin
Language(s) - English
Resource type - Journals
eISSN - 2502-1729
pISSN - 2088-088X
DOI - 10.29303/d.v1i2.117
Subject(s) - materials science , metallurgy , pitting corrosion , stress corrosion cracking , cracking , corrosion , peening , carbon steel , intergranular corrosion , composite material , residual stress
The aim of this study is to investigate the effect of shot peening on stress corrosion cracking of a low carbon steel in ocean water environment. The dimension of specimens were prepared in accordance with the ASTM G39. The hardness testing was carried out using microvickers with 0,25 kgf load in the longitudinal direction. The corrosion cracking test was immersed into artificial sea water for about 7 months. The test shows that the pitting corrosion is dominantly nucleated at the metal film interface. The biggest pitting corrosion was occurred under the static loading of 70 for the specimens unpeened. The presence of pitting corrosion promotes stress corrosion cracking. The cracking has a intergranular branched morphology which is typical for the chloride cracking of low carbon steel

The content you want is available to Zendy users.

Already have an account? Click here to sign in.
Having issues? You can contact us here