Open AccessThe Effects of TDI on Selected Properties of Ester Epoxy Alkyd Varnish
Author(s) -
Nguyễn Trung Thành
Publication year - 2020
Publication title -
tạp chí khoa học đại học quốc gia hà nội: khoa học tự nhiên và công nghệ (vnu journal of science:natural sciences and technology)
Language(s) - English
Resource type - Journals
eISSN - 2615-9317
pISSN - 2588-1140
DOI - 10.25073/2588-1140/vnunst.4933
Subject(s) - alkyd , varnish , epoxy , dielectric , materials science , composite material , toluene diisocyanate , electrical resistivity and conductivity , dielectric strength , solvent , dielectric loss , polymer chemistry , chemistry , coating , organic chemistry , electrical engineering , polyurethane , optoelectronics , engineering
This article presents the effects of toluene diisocyanate (TDI) on electrical properties of ester epoxy alkyd varnish. Through testing on breakdown voltage, dielectric constant, block resistivity, Tang (Tg) dielectric loss, the electrical properties of varnish were investigated. When TDI amount increased from to 4 - 10 (w/100w of epoxy resin), the breakdown voltage increased from 21.78 to 65.69 KV/mm. With TDI of 8 - 10 w/w, the dielectric constant was the best, about 2.78 - 3.02. With TDI of 8 w/w, the block resistivity was 6.8.1014 W.cm and Tg dielectric loss was 0.0069. The article also presents the effect of TDI on solvent- and heat resistance of the varnish.