Open AccessPENGARUH KONSENTRASI INHIBITOR KOROSI EKSTRAK KULIT PISANG KEPOK (Musa paradisiaca L) TERHADAP LAJU KOROSI BAJA KARBON API 5L PADA SUHU PERENDAMAN 40OC DAN 80OC
Author(s) -
Titan Nurahman,
Ediman Ginting Suka,
Leni Rumiyanti
Publication year - 2021
Publication title -
jurnal teori dan aplikasi fisika/jurnal teori dan aplikasi fisika
Language(s) - English
Resource type - Journals
eISSN - 2549-1156
pISSN - 2303-016X
DOI - 10.23960/jtaf.v9i2.2719
Subject(s) - corrosion , immersion (mathematics) , nuclear chemistry , scanning electron microscope , musa × paradisiaca , carbon steel , materials science , metallurgy , chemistry , composite material , food science , mathematics , pure mathematics
Research has been carried out on the effect of the concentration of Kepok banana peel extract as an inhibitor on API 5L carbon steel in 3% NaCl corrosive medium. API 5L carbon steel immersion was carried out for 7 hours with two variations of immersion temperature, namely 40 and 80 oC and five variations in the concentration of corrosion inhibitors, namely 0%, 2%, 4%, 6%, 8%. Corrosion rate testing was carried out using the weight loss method. The results showed that the largest corrosion rates at immersion temperatures of 40 and 80 oC were at 0% inhibitor concentrations, namely 60.91 mm / y and 86.91 mm / y. Meanwhile, the lowest corrosion rate was at the inhibitor concentration of 8% at immersion temperatures of 40 and 80 oC, namely 32.51 mm / y and 63.92 mm / y. The greatest effectiveness of corrosion inhibitors occurred at a concentration of 8% at immersion temperatures of 40 and 80 oC of 56.63%, and 26.44%. The results of the X-Ray Diffraction (XRD) characterization showed that the phase formed was pure Fe. Scanning Electron Microscopy (SEM) characterization showed uneven clusters and smaller size, holes and cracks were also less in 8% inhibitor at immersion temperature of 40 and 80 oC compared to inhibitor 0% at immersion temperature 40 and 80 oC.