Open AccessComparison of the structural and photo-catalytic properties of nanostructured Fe3O4/TiO2 core-shell composites synthesized by ultrasonic and Stöber methods
Author(s) -
Faezeh Parast,
Mehdi Montazeri-Pour,
Masoud Rajabi,
Fatemeh Bavarsiha
Publication year - 2020
Publication title -
science of sintering/science of sintering
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.309
H-Index - 25
eISSN - 1820-7413
pISSN - 0350-820X
DOI - 10.2298/sos2004415p
Subject(s) - materials science , nanocomposite , scanning electron microscope , fourier transform infrared spectroscopy , transmission electron microscopy , titanium oxide , nanoparticle , catalysis , titanium , composite material , chemical engineering , nuclear chemistry , nanotechnology , metallurgy , chemistry , organic chemistry , engineering
In the present research, Fe3O4/TiO2 magnetic photo-catalytic nanocomposites with a core/shell structure were successfully synthesized using two techniques of ultrasonic and St?ber. In this way, iron oxide (II, III) nanoparticles as soft magnetic cores of this composite were prepared by utilizing a chemical method assisted by ultrasound with a Fe+3/Fe+2 molar ratio of 1.5 under the nitrogen atmosphere. Thereafter, titanium oxide coating was performed on Fe3O4 nanoparticles by using tetrabutyl orthotitanate (TBOT) and titanium isopropoxide (TTIP) precursors. The resultant nanostructures were characterized by means of X-ray powder diffraction (XRD), Fourier-transform infrared (FTIR) spectroscopy, energy dispersive X-ray (EDX) analysis, vibrating sample magnetometer (VSM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Through findings obtained from TEM examinations, the formation of core/shell nanostructure was confirmed in the prepared Fe3O4/TiO2 composites. Analysis of magnetic properties revealed that titanium oxide coating on iron oxide nanoparticles reduces saturation magnetization (Ms). The values of saturation magnetization for Fe3O4 powder and Fe3O4/TiO2 nanocomposite powders achieved via ultrasonic and St?ber methods were 60, 23 and 9 emu/g, respectively. Photo-catalytic properties of Fe3O4/TiO2 nanostructures were evaluated by the use of methylene blue dye under UV light. Results indicated that Fe3O4/TiO2 composite obtained by the St?ber method has a better photo-catalytic property as well as a decreased but acceptable magnetic separation. Degradation of methylene blue dye in the presence of photo-catalytic powder prepared by ultrasonic and St?ber procedures was 61 and 69 %, respectively, within 90 minutes of UV light exposure.