Open AccessInfluence of rare-earth additives (La, Sm and Dy) on the microstructure and dielectric properties of doped BaTiO3 ceramics
Author(s) -
Vesna Paunović,
Ljiljana Živković
Publication year - 2010
Publication title -
science of sintering/science of sintering
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.309
H-Index - 25
eISSN - 1820-7413
pISSN - 0350-820X
DOI - 10.2298/sos1001069p
Subject(s) - materials science , microstructure , dielectric , curie temperature , ceramic , doping , analytical chemistry (journal) , permittivity , grain size , dopant , mineralogy , sintering , dielectric loss , composite material , ferromagnetism , condensed matter physics , chemistry , physics , optoelectronics , chromatography
A series of La/Mn, Sm/Mn and Dy/Mn codoped BaTiO3 samples were prepared by the conventional solid state procedure with dopant concentrations ranging from 0.1 up to 2.0 at%. The specimens were sintered at 1320°C and 1350°C in an air atmosphere for two hours. The low doped samples demonstrated a mainly uniform and homogeneous microstructure with average grain sizes ranging from 0.3 μm to 5.0 μm. The appearance of secondary abnormal grains in the fine grain matrix and core-shell structure were observed in highly doped La/BaTiO3 and Dy/BaTiO3 sintered at 1350°C. The low doped samples, sintered at 1350°C, display a high value of dielectric permittivity at room temperature, 6800 for Sm/BaTiO3, 5900 for Dy/BaTiO3 and 3100 for La/BaTiO3. A nearly flat permittivity-response was obtained in specimens with 2.0 at% additive content. Using a modified Curie-Weiss law the Curie-like constant C⁄ and a critical exponent γ were calculated. The obtained values of γ pointed out the diffuse phase transformation in heavily doped BaTiO3 samples