Open AccessAcidic leaching of copper and tin from used consumer equipment
Author(s) -
Dušan Oráč,
Tomáš Havlík,
Anja Maul,
Mattias Berwanger
Publication year - 2015
Publication title -
journal of mining and metallurgy. section b, metallurgy/journal of mining and metallurgy. section b, metallurgy
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.42
H-Index - 20
eISSN - 2217-7175
pISSN - 1450-5339
DOI - 10.2298/jmmb141203019o
Subject(s) - leaching (pedology) , dissolution , tin , copper , combustion , pyrolysis , metallurgy , materials science , selective leaching , chemistry , environmental science , organic chemistry , soil water , soil science
This work is focused on studying thermal pretreatment and leaching of copper and tin from printed circuit boards (PCBs) from used consumer equipment. Thermal treatment experiments were realized with and without presence of oxygen at 300?C, 500?C, 700?C and 900?C for 30 minutes. Leaching experiments were performed at 80?C in 2M HCl in two stages. The first stage consisted of classic leaching experiments of samples without and after thermal treatment. The second stage consisted of oxidative leaching experiments (blowing of air or oxygen) with the aim to intensify metals leaching. The results of thermal treatment experiments show that maximal mass loss after burning (combustion) was 53 % (700?C) and after pyrolysis 47 % (900 %). Oxidative leaching resulted in complete dissolution of copper and tin after 60. or 90 minutes of thermally treated samples. Pyrolysis and combustion have positive effects on metals dissolution in comparison with samples without thermal pretreatment. Moreover, the dissolution of metals is more effective and needs shorter leaching time.