Open AccessDissolution mechanism of Al2O3 in refining slags containing Ce2O3
Author(s) -
L.J. Wang,
Q. Wang,
J.M. Li,
KuoChih Chou
Publication year - 2016
Publication title -
journal of mining and metallurgy. section b, metallurgy/journal of mining and metallurgy. section b, metallurgy
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.42
H-Index - 20
eISSN - 2217-7175
pISSN - 1450-5339
DOI - 10.2298/jmmb140706004w
Subject(s) - dissolution , slag (welding) , refining (metallurgy) , metallurgy , materials science , calcium , chemical engineering , chemistry , mineralogy , engineering
In the present work, the rate of dissolution of Al2O3 rod in CaO-SiO2-Al2O3 and CaO-SiO2-Al2O3-Ce2O3 slags were carried out in the temperature range of 1793 K (1520ºC) - 1853 K (1580ºC) under static conditions. The cross section of the rod and the boundary layers were identified and analyzed by SEM-EDS. The dissolution of Al2O3 was favored with the increasing CaO/Al2O3 ratio, elevating temperatures as well as the addition of Ce2O3. An intermediate product 3CaO5Al2O3Ce2O3 was detected. The mechanism of dissolution of Al2O3 in the Ce2O3 containing slag were also proposed as three steps involved: 1) the formation of calcium aluminates CaO•Al2O3 at the interface 2) the formation of 3CaO5Al2O3Ce2O3 as the reaction progresses; and 3) the dissolution of 3CaO5Al2O3Ce2O3 into the slag