Open AccessStudy for Improvement in the Surface Properties and Wear Behavior of Mild Steel
Author(s) -
Hamdan Gowhar Nahvi
Publication year - 2021
Publication title -
international journal for research in applied science and engineering technology
Language(s) - English
Resource type - Journals
ISSN - 2321-9653
DOI - 10.22214/ijraset.2021.38538
Subject(s) - materials science , base metal , metallurgy , aluminium , metal , carbon steel , base (topology) , composite material , welding , corrosion , mathematical analysis , mathematics
Surface of a material can be improved by depositing the filler metal for the enhancement of various properties. Surface should be harder than substrate material for surface improvement. This surface improvement is also known as surfacing. In present research Mild steel specimens of size 140×35×40 were used to deposit surfacing layers and study the feasibility of iron/aluminum with varying compositions on low carbon steel deposited by GTAW process. Specimens for hardness and oxidation resistance were prepared. While studying oxidation of surfaced and un-coated area (base material), oxidation test resulted that the oxidation occurred on surface of base metal (un-coated area) after heating at different temperatures and time intervals. Specimens kept at 500˚C, 700˚C temperatures for 3, 6, 9 hours to get oxidized from un-coated surface but no mark of oxidation and pitting was visible at surfaced area but pitting of un-coated area occurred at 700˚C temperature. Oxidation had no effect to surfaced area. Low temperature oxidation test specimens gave only weight loss from un-coated portion but high temperature oxidation gave high amount of weight reduction due to pitting occurred on un-coated portion. The amount of weight loss of specimens increased with increase in furnace holding time at constant temperature. With increase in temperature oxidation of un-coated area of specimens also increased and pitting action occurred on un-coated area of specimens at high temperature. Further, for the various wear tests the cylindrical pins of 8 mm diameter with spherical tip 4 mm radius was made. Wear tests were carried out on pin on disc sliding wear testing machine. The comparison of wear rate loss was studied with constant sliding distance, varying load and sliding velocity of different compositions of iron/aluminum surfacing and substrate material. Hardness and wear resistance of composition were increased with increase in percentage of Fe element in composition. Composition C1 (Fe:Al/70:30) had high hardness and high wear resistance as compared to composition C2 (Fe:Al/30:70) and C3 (Fe:Al/50:50). Composition C3 (Fe:Al/50:50) had better hardness and wear resistance as compared composition C2 (Fe:Al/70:30). Keywords: Surface improvement, Fe-Al intermetallic, GTAW process, Sliding wear.