Open AccessОсобенности зарождения и роста нитевидных нанокристаллов InGaN на подложках SiC/Si методом хлорид-гидридной эпитаксии
Author(s) -
С.А. Кукушкин,
А. В. Осипов,
Alexey Redkov,
В.М. Стожаров,
E. V. Ubyĭvovk,
Sh. Sh. Sharofidinov
Publication year - 2022
Publication title -
pisʹma v žurnal tehničeskoj fiziki
Language(s) - English
Resource type - Journals
eISSN - 1726-7471
pISSN - 0320-0116
DOI - 10.21883/pjtf.2022.04.52080.19056
Subject(s) - nanocrystal , nucleation , materials science , metal , nanotechnology , chemical physics , crystallography , metallurgy , chemistry , organic chemistry
The growth of InGaN layers on hybrid SiC/Si substrates with orientations (100), (110), and (111) by the HVPE method was studied at temperatures that wittingly exceed the temperature of InN decomposition onto nitrogen atoms and metallic In (1000C). On substrates with orientations (110) and (111), the formation of InGaN nanocrystals was observed. The shape and growth mechanisms of nanocrystals were investigated. It is shown that nanocrystals nucleate on the (111) surface only inside V-defects formed at the points where screw dislocations exit onto the surface. On the (110) surface, nanocrystals are formed only on pedestals that arise during the film growth. An explanation is given for the difference in the growth mechanisms of nanocrystals on substrates of different orientations.