Open AccessCOMPLEX MODIFICATION OF GRAY CAST IRON
Author(s) -
О. С. Комаров,
Е. В. Розенберг,
К. Э. Барановский
Publication year - 2017
Publication title -
litʹë i metallurgiâ
Language(s) - English
Resource type - Journals
eISSN - 2414-0406
pISSN - 1683-6065
DOI - 10.21122/1683-6065-2017-1-16-20
Subject(s) - cast iron , gray iron , metallurgy , materials science , foundry
The influence of the complex modifier by chemical – active and surface-active additives of gray cast iron on the size of chill and on the width of molted iron zone was researched. The width of a chill zone and molted iron zones were measured at chank ends of various diameter cores. The cores were casted on a massive steel plate and also in standard chill tests. It was established that additional adding of surface-active bismuth in structure of various graphitizing modifiers promoted to reduce the width a chill zone and molted iron zones. It was established that the complex modifiers consisting of chemical – active and surfaceactive components are effective in fight with chill in cast iron castings and can be recommended for application in foundry shops of the entities of a machine-building profile for production of high-quality castings.