Open AccessEffect of hydrogen peroxide application on color and surface roughness of two restorative materials
Author(s) -
Dilcele Silva Moreira Dziedzic,
Lucia Helena Ramos da Silva,
Bruna Luiza do Nascimento,
Marina Samara Baechtold,
Gisele Maria Correr,
Carla Castiglia Gonzaga
Publication year - 2017
Publication title -
brazilian journal of oral sciences/brazilian journal of oral sciences
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.125
H-Index - 11
eISSN - 1677-3225
pISSN - 1677-3217
DOI - 10.20396/bjos.v15i3.8649978
Subject(s) - polishing , lightness , surface roughness , materials science , glass ionomer cement , composite material , surface finish , cement , hydrogen peroxide , colorimeter , lacquer , optics , coating , chemistry , physics , organic chemistry
Aim: This study investigated the effect of an in-office bleaching technique on lightness, color and surface roughness of two commercially available materials: a resin-modified glass-ionomer cement and a nanohybrid resin composite. Methods: Twelve disk-shaped specimens were prepared with both materials. The samples were bleached with 35% hydrogen peroxide. Bleaching was tested initially onto a smooth surface and later onto a polished one of the same specimens. The effect of the treatments on lightness and color was verified with a spectrophotometer. Surface roughness was measured with a digital surface roughness tester. The data were statistically analyzed by repeated measures ANOVA and post hoc Tukey’s test (alpha = 0.05). Results: Significant variation in lightness and color was observed on the resin-modified glass-ionomer cement after the first bleaching procedure. Roughness increased significantly only after polishing the resin-modified glass-ionomer cement surface. Composite color variation was evident in the last observation period, but roughness and lightness variation due to bleaching and polishing was not significant. Conclusion: The bleaching treatment caused significant color alterations on the materials tested. This study observed that the application of in-office bleaching onto the glass-ionomer cement promoted clinically observable color alteration, and polishing after bleaching is contraindicated for this material.