Open AccessInfluence of different surface treatments of fiberglass posts on the bond strength to dentin
Author(s) -
Bruna Cristina do Nascimento Rechia,
Ruth Peggy Bravo,
Naylin Danyele de Oliveira,
Flares BarattoFilho,
Carla Castiglia Gonzaga,
Carmen Lúcia Mueller Storrer
Publication year - 2017
Publication title -
brazilian journal of oral sciences/brazilian journal of oral sciences
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.125
H-Index - 11
eISSN - 1677-3225
pISSN - 1677-3217
DOI - 10.20396/bjos.v15i2.8648768
Subject(s) - bond strength , dentin , materials science , distilled water , silane , dentistry , adhesive , composite material , chemistry , medicine , layer (electronics) , chromatography
Aim: To assess the influence of different fiberglass post surface treatments on the bond strength (BS) to root dentin. Methods: Thirty bovine root canals were endodontically treated and filled with gutta-percha and AH Plus sealer. At 24 h after the endodontic filling, the post spaces were prepared with Gates-Glidden drills and #3 drills of the DC White Post system, maintaining a 4 mm apical seal. The roots were randomly divided into three groups: S (fiberglass posts treated with silane), SA (fiberglass posts treated with silane and a hydrophobic adhesive system) and SHA (fiberglass posts treated with silane, followed by drying with hot air). The posts were cemented with a selfadhesive cement (RelyX U200). The specimens were stored in distilled water at 37 °C for 24 h and subjected to the push-out test (0.5 mm/min). Data were statistically analyzed using one-way ANOVA and Tukey's test (α=0.05) Results: SA and SHA groups showed the highest BS mean values (11.29 and 10.85 MPa, respectively), while the S group presented the lowest BS mean value (7.21 MPa). S group was significantly different from SA and SAH groups. Conclusions: The surface treatment of fiberglass posts influenced BS values.