Open AccessSynthesis of nanostructured (Ti-Zr-Si)N coatings deposited on Ti6Al4V alloy
Author(s) -
Leydi Julieta Cardenas-Flechas,
Claudia Patricia Mejía-Villagrán,
Miryam R. Joya,
J.J. Olaya
Publication year - 2021
Publication title -
revista de la academia colombiana de ciencias exactas físicas y naturales
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.124
H-Index - 2
eISSN - 2382-4980
pISSN - 0370-3908
DOI - 10.18257/raccefyn.1198
Subject(s) - materials science , scanning electron microscope , alloy , titanium alloy , adhesive , phase (matter) , metallurgy , diffraction , composite material , optics , chemistry , layer (electronics) , physics , organic chemistry
d Zr targets. The synthesis of the coatings was carried out by varying the discharge power in the Ti5 well as a variation in the deposit temperature at room temperature 130° and 260°C. The coatings were characterized by means of X-ray diffraction (XRD), evidencing the formation of the phase that belongs to the solid solution (Zr, Ti)N, scanning electron microscopy (SEM), UV-Vis spectroscopy and hardness and pin-on-disc tests. The thickness was measured through interferometry with values between 662 and 481nm for the deposited coatings. According to the failure mechanism in the scratch test, the best results were obtained with a power of 170W and 260°C with a cohesive failure Lc1 = 2.1N and an adhesive failure Lc2 = 4.7N.
Accelerating Research
Robert Robinson Avenue,
Oxford Science Park, Oxford
OX4 4GP, United Kingdom
Address
John Eccles HouseRobert Robinson Avenue,
Oxford Science Park, Oxford
OX4 4GP, United Kingdom