Open AccessA EFFECT OF CeO2 DOPING ON THE MICROSTRUCTURE AND CORROSION BEHAVIOR OF CoCuNiTi HIGH-ENTROPY ALLOY COATINGS
Author(s) -
Minglin Ma,
Liang Zhao,
Zhixin Wang,
Li Shangzhi,
Dong Chen
Publication year - 2021
Publication title -
materiali in tehnologije
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.27
H-Index - 25
eISSN - 1580-3414
pISSN - 1580-2949
DOI - 10.17222/mit.2021.286
Subject(s) - materials science , microstructure , corrosion , scanning electron microscope , alloy , composite material , nucleation , doping , high entropy alloys , metallurgy , phase (matter) , thermodynamics , optoelectronics , physics , chemistry , organic chemistry
CoCuNiTi high-entropy alloy coatings with an equal molar ratio were prepared on 45 steel substrates using the laser-cladding method. The effect of CeO2 doping on phase structure, microstructure and corrosion behavior of CoCuNiTi coatings were investigated by X-ray diffraction, optical microscope, scanning electron microscope, and electrochemical workstation. The results show that the phase structure of CoCuNiTi coating doped with 1 w/% CeO2 is transformed from the original dual-phase structure of FCC main phase and BCC phase to the dual-phase structure of BCC main phase and FCC phase, mainly because CeO2 addition helps to improve the temperature gradient and solidification rate during solidification, reduce the nucleation resistance and the diffusion distance of the alloying elements, and provide a liquid environment with longer time, lower viscosity and higher diffusion rate. The microstructure of the two coatings is composed of BCC-phase dendrite and FCC-phase interdendrite. The widths of the primary dendrites of the columnar dendrites in CoCuNiTi cladding layer before and after CeO2 doping are about 8.10 µm and 6.51 µm, respectively. The CoCuNiTi coating doped with 1 w/% CeO2 has the smallest corrosion current density, the largest capacitive reactance arc radius and polarization resistance, and the best corrosion resistance in 3.5 w/% NaCl solution, which is mainly due to making the alloy structure refined and the element distribution uniform after the CeO2 addition.