Characterization of high-energy milled alumina powders

The utilization of reactive high-energy milling has been reported for the synthesis of ceramic powders namely, metal oxides, carbides, borides, nitrides or mixtures of ceramics or ceramic and metal compounds. In this work, high-energy milling was used for reduction of alumina powders to nanometric particle size. The ceramic characteristics of the powders were analyzed in terms of the behavior during deagglomeration, compaction curves, sintering and microstructure characterization. It was observed that the high energy milling has strong effect in producing agglomeration of the nanosized powders. This effect is explained by the high-energy impact of the balls, which may fracture particles or just cause the particles compacting. In this case, strong agglomerates are produced. As the powder surface area increases, stronger agglomerates are produced. Tem sido amplamente divulgada a utilização da moagem reativa de alta energia para a síntese de pós cerâmicos de óxidos de metais, carbetos, boretos, nitretos ou misturas de compostos cerâmicos ou compostos cerâmicos e metálicos. Neste trabalho, a moagem de alta energia (não reativa) foi utilizada para a redução de pós de alumina para partículas de dimensões nanométricas. As características cerâmicas dos pós obtidos foram analisadas a partir de resultados de comportamento durante a desaglomeração, curvas de densificação, sinterização e caracterização de microestrutura. Observou-se que a moagem de alta energia tem forte efeito de aglomeração dos pós com partículas em dimensões nanométricas. Esse efeito é explicado pelo impacto de alta energia das bolas, os quais podem fraturar as partículas ou apenas causar a compactação das mesmas. Nesse último caso, que sempre ocorre, são formados aglomerados de alta resistência. O aumento da área superficial do pó produz aglomerados mais resistentes