Open AccessAnalisis Kuat Tekan Beton Dengan Penambahan Serat Rooving Pada Beton Non Pasir
Author(s) -
Achmad Widodo,
Muhammad Abdil Basith
Publication year - 2017
Publication title -
jurnal teknik sipil dan perencanaan/jurnal teknik sipil dan perencanaan
Language(s) - English
Resource type - Journals
eISSN - 2503-1899
pISSN - 1411-1772
DOI - 10.15294/jtsp.v19i2.12138
Subject(s) - compressive strength , materials science , fiber , composite material , ultimate tensile strength , physics
This study aims to determine the effect of adding roving fiber on non-sand concrete to compressive strength and tensile strength. The test specimens used in this study, for each type of variable are 3 cylinders of compression test. The ratio of the volume of mortar is 1: 5 (cement: gravel) while the roving fiber used is 3 cm in length. the addition of roving fibers of each mixture of 0%, 2.5%, 5%, 7.5%, 10% were taken from the weight of the cement. From the results of the research it is found that the addition of roving fiber can increase the compressive strength of non-sand concrete. With the addition of compressive strength concrete roving with an aggregate ratio of 1: 5, it is optimal on the percentage of roving fiber addition of 5%.Penelitian ini bertujuan untuk mengetahui pengaruh penambahan serat roving pada beton non pasir terhadap kuat tekan dan kuat tarik belahnya. Hasil penelitian ini diharapkan menjadi masukan bagi khalayak umum khususnya bagi industri bahan bangunan, dan dapat bermanfaat untuk peneliti-peneliti selanjutnya. Benda uji yang digunakan dlam penelitian ini, untuk masing-masing jenis variable berupa 3 silinder uji tekan. Perbandingan volume adukan adalah 1:5 (semen:kerikil) sedang serat roving yang digunakan panjangnya 3 cm. Penambahan serat roving masing-masing adukan sebanyak 0% , 2.5% , 5% , 7.5% , 10 % diambil dari berat semen. Dari hasil penelitian didapat bahwa penambahan serat roving dapat meningkatkan kuat tekan beton non pasir. Dengan penambahan serat roving kuat tekan beton dengan perbandingan agregat 1:5 , optimal pada persentase penambahan serat roving sebesar 5% .