Open AccessNew Trends in Dentin Bonding: Treatment with chlorhexidine, hyaluronic acid, vitaminc C and green tea
Author(s) -
Beatriz Maria da Fonseca,
Patrícia Rondon Pleffken,
Ivan Balducci,
Franklin R. Tay,
Cesar Rogério Pucci,
Maria Amélia Máximo de Araújo
Publication year - 2013
Publication title -
brazilian dental science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.153
H-Index - 6
ISSN - 2178-6011
DOI - 10.14295/bds.2013.v16i3.876
Subject(s) - bond strength , dentin , chlorhexidine , chemistry , distilled water , hyaluronic acid , dentistry , adhesive , single bond , acrylic resin , nuclear chemistry , universal testing machine , dental bonding , buccal administration , ultimate tensile strength , materials science , chromatography , composite material , medicine , group (periodic table) , coating , layer (electronics) , organic chemistry , anatomy
Objective: The aim of this study was to evaluate the bond strength of dentin treated with chlorhexidine, hyaluronic acid, vitamin C and green tea. Material and Methods: The roots of 50 bovine teeth were removed and buccal coronal dentin was exposed. After acid-etching, the specimens were divided into 5 groups (n = 10), according to the dentin treatment strategy: CO - untreated dentin; CHX - treated with 2 wt% chlorhexidine for 30 sec; HA - treated with 1 wt% hyaluronic acid for 30 sec; VC - treated with 10 wt% vitamin C for 30 sec; GT - treated a 1% green tea extract for 30 sec. Adper Single Bond was then applied to the treated according to the manufacturer's recommendations. The specimens were restored with a 4-mm thick layer of the resin composite, which was polymerized for 40 sec. The specimens were stored in distilled water at 37°C for 24 h and sectioned into 1x1 mm2 sticks containing the adhesive interface. Microtensile bond strength testing was performed with a universal testing machine at a cross-head speed of 1.0 mm/min. Results: The results were analyzed with one-factor ANOVA and Tukey’s multiple comparison tests. GT group presented the highest values bond strength (29.4±3.1)a, but no significant difference compared to the other experimental groups HA(26.7±3.1)ab, CHX(25.4±2.6)ab and VC(22.4±6.0)b. Bond strengths of experimental groups were not significantly different from the CO. Conclusion: Immediate bond strength was preserved after acid-etched dentin was treated.Keywords: Chlorhexidine. Hyaluronic acid. Vitamin C. Green tea. Bond strength.