Open AccessEfficacy of fluoride varnishes for preventing enamel demineralization after interproximal enamel reduction. Qualitative and quantitative evaluation
Author(s) -
Ascensión Vicente,
Antonio José Ortiz Ruiz,
Belén Manuela González Paz,
Juan Ramírez López,
Luis Alberto Bravo González
Publication year - 2017
Publication title -
plos one
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.99
H-Index - 332
ISSN - 1932-6203
DOI - 10.1371/journal.pone.0176389
Subject(s) - demineralization , enamel paint , fluoride , remineralisation , dentistry , chemistry , scanning electron microscope , varnish , fluoride varnish , nuclear chemistry , materials science , medicine , inorganic chemistry , composite material , organic chemistry , coating
Objectives To evaluate quantitatively and qualitatively the changes produced to enamel after interproximal reduction and subjected to demineralization cycles, after applying a fluoride varnish (Profluorid) and a fluoride varnish containing tricalcium phosphate modified by fumaric acid (Clinpro White). Materials and methods 138 interproximal dental surfaces were divided into six groups: 1) Intact enamel; 2) Intact enamel + demineralization cycles (DC); 3) Interproximal Reduction (IR); 4) IR + DC; 5) IR + Profluorid + DC; 6) IR + Clinpro White + DC. IR was performed with a 0.5 mm cylindrical diamond bur. The weight percentage of calcium (Ca), phosphorous (P) and fluoride (F) were quantified by energy-dispersive X-ray spectrometry (EDX). Samples were examined under scanning electron microscopy (SEM). Results The weight percentage of Ca was significantly higher (p<0.05) in Groups 1, 2 and 5 than Groups 4 and 6. No significant differences were detected in the weight percentage of Ca between Group 3 and the other groups (p>0.05). The weight percentage of P was similar among all six groups (p>0.05). F was detected on 65% of Group 6 surfaces. SEM images of Groups 4 and 6 showed signs of demineralization, while Group 5 did not. Conclusions Profluorid application acts as a barrier against the demineralization of interproximally reduced enamel.