Open AccessCorrosion Behavior of Mg(OH)2/Mg–Al Layered Double Hydroxides/AlO(OH) Composite Film Prepared by Steam Coating on Mg Alloy AZCa612
Author(s) -
Kae Nakamura,
Yoshiki Nagashima,
Hiraku Muto,
Ryo Nakano,
Takahiro Ishizaki
Publication year - 2022
Publication title -
journal of the electrochemical society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 1.258
H-Index - 271
eISSN - 1945-7111
pISSN - 0013-4651
DOI - 10.1149/1945-7111/ac54db
Subject(s) - corrosion , materials science , dielectric spectroscopy , alloy , layered double hydroxides , scanning electron microscope , polarization (electrochemistry) , fourier transform infrared spectroscopy , immersion (mathematics) , aqueous solution , magnesium alloy , coating , electrochemistry , metallurgy , chemical engineering , nuclear chemistry , composite material , chemistry , mathematics , electrode , pure mathematics , engineering , hydroxide
This study investigated the corrosion behavior of the corrosion-resistant films steam coated on AZCa612 magnesium alloy. The film samples were corroded by immersing them in 5 wt% NaCl aqueous solution for a predetermined time. The corroded films were characterized using scanning electron microscopy, energy-dispersive X-ray spectroscopy, glancing angle X-ray diffraction, Fourier transform infrared spectroscopy, potentiodynamic polarization measurements, hydrogen generation measurements, and electrochemical impedance spectroscopy. The amount of Mg–Al–CO 3 layered double hydroxides (LDHs) in the film slightly decreased from the beginning of immersion to 120 h after immersion and gradually increased thereafter. Mg–Al–Cl LDHs were formed after 6 h of immersion and rapidly grew as the immersion progressed. In addition, even with the gradual decrease in the corrosion resistance of the film, there was no major damage observed on the substrates. These results indicate that the corrosion protection mechanism varied with the immersion time. The corrosion-resistant property under a short immersion time could be attributed to the high corrosion resistance of Mg(OH) 2 and AlO(OH), whereas it is attributed to the coverage provided by the Mg–Al–Cl and Mg–Al–CO 3 LDHs under a longer immersion duration.