Corrosion of concrete reinforcement and electrochemical factors in concrete patch repair

Corrosion of concrete reinforcement at a patch repair is a complex problem, and current knowledge of its mechanism is quite limited. This review examined the correlation between two corrosion mechanisms, macrocell and microcell corrosion, from fundamental electrochemical principles. It was found that both mechanisms could play significant roles in inducing corrosion damage, contrary to the prevailing opinion that macrocell corrosion is the main deterioration mechanism in patch repair. This has practical implications that need to be considered for an effective and durable repair. A review of the studies done to date also enabled the identification of the key factors in patch repair controlling the corrosion characteristics. Corrosion could occur at different locations in the vicinity of the patch ? substrate, interface, or patch area ? depending on the respective electrochemical environments induced by the repair material properties and treatments, as well as the in-service exposure and mechanical loading. The review indicates that much of the needed research should focus on identification of corrosion mechanisms to effect successful patch repair in reinforced concrete structures.La corrosion de l'armature pour b\ue9ton lors d'un rapi\ue9\ue7age est une question complexe et les connaissances actuelles de ce m\ue9canisme sont assez limit\ue9es. Le pr\ue9sent article \ue9tudie la corr\ue9lation entre deux m\ue9canismes de corrosion, la corrosion des macrocellules et la corrosion des microcellules, du point de vue des principes \ue9lectrochimiques fondamentaux. Il a \ue9t\ue9 d\ue9couvert que les deux m\ue9canismes peuvent jouer un r\uf4le important dans l'apparition des dommages dus \ue0 la corrosion, contrairement \ue0 l'opinion courante voulant que la corrosion des macrocellules est le principal m\ue9canisme de d\ue9t\ue9rioration lors des rapi\ue9\ue7ages. Cela pr\ue9sente des applications pratiques \ue0 consid\ue9rer pour une r\ue9paration efficace et durable. Un examen des \ue9tudes effectu\ue9es \ue0 ce jour a \ue9galement permis d'identifier les facteurs cl\ue9s pour contr\uf4ler les caract\ue9ristiques de la corrosion lors de rapi\ue9\ue7ages. La corrosion peut survenir \ue0 divers endroits ?\ue0 proximit\ue9 du rapi\ue9\ue7age : substrat, interface ou zone du rapi\ue9\ue7age ? selon les environnements \ue9lectrochimiques respectifs induits par les propri\ue9t\ue9s des mat\ue9riaux et des traitements de rapi\ue9\ue7age, ainsi que par l'exposition durant le service et la charge m\ue9canique. L'examen indique qu'une grande partie de la recherche requise devrait porter sur l'identification des m\ue9canismes de corrosion afin d'effectuer des rapi\ue9\ue7ages r\ue9ussis dans les structures en b\ue9ton arm\ue9.Peer reviewed: YesNRC publication: Ye