SU‐F‐T‐550: Radiochromic Plastic Thin Sheet Dosimeter: Initial Performance
Author(s) -
Jordan K,
Adamovics J
Publication year - 2016
Publication title -
medical physics
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 1.473
H-Index - 180
eISSN - 2473-4209
pISSN - 0094-2405
DOI - 10.1118/1.4956735
Subject(s) - dosimeter , materials science , densitometer , optics , dosimetry , sensitivity (control systems) , irradiation , attenuation , scanner , nuclear medicine , optoelectronics , medicine , physics , engineering , electronic engineering , nuclear physics
Purpose: Thin sheets, of a high sensitivity formulation of radiochromic dosimeter, Presage were prepared and evaluated for optical readout. Methods: Sheets of radiochromic polyurethane, 12 cm long, 10 cm wide and 0.2 cm thick were prepared with leuco crystal violet as the reporter molecule. Sample transmission was evaluated at a wavelength of 590 nm with in‐house constructed instruments: optical cone beam laser CT scanner, fixed and scanning spot densitometers. Sample sequential irradiations to a total dose of 40 Gy were conducted with a modified, Theratron 60, cobalt radiotherapy machine at dose rates of 1 or 0.25 Gy per minute. Exposure to ambient and readout light was minimized to limit background photochromic signals. Samples were stored at 4°C. Optical activity was assessed from linearly polarized transmission images. Comparison sensitivity measurements with EBT3 film were conducted. Results: Samples were transparent, smooth and pale purple before irradiation. Radiochromic reaction was completed in less than 5 minutes. A linear dose response with a sensitivity of 0.5 cm‐1Gy‐1 was observed. Micrometer measurements found sheet thickness variations up to 20%. Uniform dose, 2 Gy attenuation images, correlated with local sheet thicknesses. Comparable measurements with EBT3 film were 3 times more sensitive at 1 Gy but above 15 Gy, EBT3 film had lower sensitivity than 0.2 cm thick Presage sheet dosimeter due to its non‐linear response. Conclusion: Dose sensitivity provided a 10% decrease in transmission for a 1 Gy dose. Improvements in mold design are expected to allow production of sheets with less than 5% variation in thickness. Above, 10 Gy, Presage sheet dosimeter performance expected to exceed EBT3 film based on linearity, sensitivity, transparency and smoothness of samples. J Adamovics is owner of Heuris Inc