Experimental Investigation of Strain Behaviour of Heated Cement Paste and Concrete
Author(s) -
Ring T.,
Zeiml M.,
Lackner R.,
Eberhardsteiner J.
Publication year - 2013
Publication title -
strain
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.477
H-Index - 47
eISSN - 1475-1305
pISSN - 0039-2103
DOI - 10.1111/str.12032
Subject(s) - spall , materials science , composite material , cement , modulus , stress–strain curve , compressive strength , thermal , material properties , elastic modulus , structural engineering , deformation (meteorology) , physics , meteorology , engineering
The material degradation of concrete subjected to fire events has a severe influence on the load‐carrying capacity of support structures. Spalling of concrete layers, exposing the reinforcement bars and degradation of the material properties (Young's modulus, compressive strength) may lead to significant damage of the reduced cross‐section and, therefore, cause failure of the structure. In order to understand the stress build‐up at the heated surface caused by thermal expansion due to fire loading, finally leading to damage and spalling of concrete, the strain behaviour of cement paste and concrete exposed to combined thermo‐mechanical loading is the focus of this work. Hereby, the evolution of thermal strains, Young's modulus and Poisson's ratio with increasing temperature are investigated experimentally. For this purpose, the specimens are loaded uniaxially while the temperature is increased up to 800 °C. The obtained results provide the proper basis for the development of realistic material models, allowing more sophisticated simulations of structures exposed to fire.