The combined influence of Mg and Ca on microstructural evolution of alumina
Author(s) -
Moshe Ruth,
Kaplan Wayne D.
Publication year - 2019
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/jace.16321
Subject(s) - solubility , spinel , scanning electron microscope , grain boundary , analytical chemistry (journal) , materials science , mineralogy , nuclear chemistry , chemistry , microstructure , metallurgy , chromatography , composite material
The solubility limits of Ca and Mg co‐doped in alumina at 1600°C were determined by equilibrating alumina saturated with Ca and Mg. This resulted in the formation of MgAl 2 O 4 (Mg spinel), CaO·6Al 2 O 3 (CA6), Ca 2 Mg 2 Al 28 O 46 (CAM‐II), and alumina grains saturated with Mg and Ca. Under these conditions, the amount of Ca and Mg in the alumina grains represents the solubility limits. The solubility limits were measured using a fully standardized wavelength dispersive spectrometer mounted on a scanning electron microscope. In the co‐doped state, the solubility limit of Ca in alumina was 32 ± 13 ppm, and the solubility limit of Mg in alumina was 210 ± 43 ppm. The presence of Ca results in an increase of the solubility limit of Mg in alumina from 132 to 210 ppm, suggesting that the increased Mg in solution results in more Mg excess at the alumina grain boundaries, thus contributing to a decreased grain‐boundary mobility by solute‐drag.