Microstructure–conductivity relationship of Na 3 Zr 2 (SiO 4 ) 2 (PO 4 ) ceramics
Author(s) -
Naqash Sahir,
Sebold Doris,
Tietz Frank,
Guillon Olivier
Publication year - 2019
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/jace.15988
Subject(s) - microstructure , sintering , materials science , grain boundary , conductivity , ionic conductivity , analytical chemistry (journal) , grain growth , activation energy , electrical resistivity and conductivity , scanning electron microscope , grain size , mineralogy , ceramic , dielectric spectroscopy , composite material , electrolyte , chemistry , electrical engineering , electrode , chromatography , electrochemistry , engineering
Abstract The ionic conductivity of solid electrolytes is dependent on synthesis and processing conditions, ie, powder properties, shaping parameters, sintering time ( t s ), and sintering temperature ( T s ). In this study, Na 3 Zr 2 (SiO 4 ) 2 (PO 4 ) was sintered at 1200 and 1250°C for 0‐10 hours and its microstructure and electrical performance were investigated by means of scanning electron microscopy and impedance spectroscopy. After sintering under all conditions, the sodium super‐ionic conductor‐type structure was formed along with ZrO 2 as a secondary phase. The microstructure investigation revealed a bimodal particle size distribution and grain growth at both T s . The density of samples increased from 60% at 1200°C for 0 hours to 93% at 1250°C for 10 hours. The ionic conductivity of the samples increased with t s due to densification and grain growth, ranging from 0.13 to 0.71 mS/cm, respectively. The corresponding equivalent circuit fitting for the impedance spectra revealed that grain boundary resistance is the prime factor contributing to the changing conductivity after sintering. The activation energy of the bulk conductivity ( E a,bulk ) remained almost constant (0.26 eV) whereas the activation energy of the total conductivity ( E a ) exhibited a decreasing trend from 0.37 to 0.30 eV for the samples with t s = 0 and 10 hours, respectively—both sintered at 1250°C. In this study, the control of the grain boundaries improved the electrical conductivity by a factor of 6.