Premium
Tuning Mn 4+ Red Photoluminescence in (K,Rb) 2 Ge 4 O 9 :Mn 4+ Solid Solutions by Partial Alkali Substitution
Author(s) -
Li Pengfei,
Wondraczek Lothar,
Peng Mingying,
Zhang Qinyuan
Publication year - 2016
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/jace.14363
Subject(s) - photoluminescence , isostructural , luminescence , crystallography , phosphor , solid solution , alkali metal , octahedron , crystal structure , materials science , chemistry , analytical chemistry (journal) , optoelectronics , organic chemistry , chromatography , metallurgy
We report on intense photoluminescence from materials of the (Rb,K) 2 Ge 4 O 9 :Mn 4+ solid solution as a novel class of red‐emitting oxide phosphors. In these compounds, luminescence originates from a virtually ideal substitution of Mn 4+ for Ge 4+ on octahedral lattice sites which are well‐isolated from each other within the unit cell by intermediate GeO 4 species. Complete isostructural substitution of K for Rb is possible across the join. The associated slight shrinkage of the unit cell has only little effect on the apparent Mn 4+ interionic distance, but enables tuning of the absorption cross section and of the band structure, hence, of the emission lifetime, of the excitation band shape, and of emission quantum yield. Partial substitution was also found to reduce thermal quenching of the Mn 4+ ‐related emission, apparently due to the lower polarizability of the K + ion. In addition, random substitution of Rb by K enables modulation of the interaction of Mn 4+ with its surrounding field at lower symmetry, leading to increasing emission bandwidth, i.e., 595 cm −1 in K 1.5 Rb 0.5 Ge 4 O 9 :Mn 4+ vs 558 or 578 cm −1 in Rb 2 Ge 4 O 9 :Mn 4+ or K 2 Ge 4 O 9 :Mn 4+ respectively.