High‐Energy Mechanical Treatment Boosts Ion Transport in Nanocrystalline Li 2 B 4 O 7
Author(s) -
Wohlmuth Dominik,
Epp Viktor,
Stanje Bernhard,
Welsch AnnaMaria,
Behrens Harald,
Wilkening Martin
Publication year - 2016
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/jace.14165
Subject(s) - crystallite , nanocrystalline material , materials science , amorphous solid , ion , ionic conductivity , conductivity , ionic bonding , analytical chemistry (journal) , crystallography , nanotechnology , chemistry , metallurgy , organic chemistry , chromatography , electrode , electrolyte
In many cases fast solid ion conductors are characterized by a large number fraction of defects and vacant positions that enable the ions to move over long distances in a facile way. The introduction of structural disorder via high‐energy mechanical impact represents a very promising possibility to improve and to tune the transport properties of otherwise poorly conducting solids. Lithium tetraborate, Li 2 B 4 O 7 , in its single crystalline form or with an average crystallite size in the μm range, is known as a very poor Li ion conductor and can serve as a model compound to study the influence of structural disorder on ion dynamics. In the present study, we used high‐energy ball milling to prepare nanocrystalline defect‐rich Li 2 B 4 O 7 characterized by a mean crystallite diameter of ca. 20 nm. With increasing milling time the sample became partly amorphous. Polycrystalline Li 2 B 4 O 7 with crystallite sizes in the order of 100 nm served as starting material. The nanostructured samples obtained show dc conductivities σ dc in the order of 2.5 × 10 −7 S/cm at 490 K which represents an increase by more than four orders of magnitude compared to the source material. While conductivity spectroscopy was applied to study the effect of different milling times on ionic conductivity in detail; Li ion self‐diffusion in nanostructured Li 2 B 4 O 7 as well as in the starting material was investigated by variable‐temperature solid‐state 7 Li nuclear magnetic resonance ( NMR ) relaxometry. While the first is sensitive to long‐range ion transport, lithium NMR is able to access also short‐ranged ion motions.