Thermal Expansion, Heat Capacity, and Thermal Conductivity of Nickel Ferrite (NiFe 2 O 4 )
Author(s) -
Nelson Andrew T.,
White Joshua T.,
Andersson David A.,
Aguiar Jeffery A.,
McClellan Kenneth J.,
Byler Darrin D.,
Short Michael P.,
Stanek Christopher R.
Publication year - 2014
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/jace.12901
Subject(s) - materials science , thermal conductivity , thermal diffusivity , curie temperature , heat capacity , nucleation , atmospheric temperature range , thermal expansion , nickel , ferrite (magnet) , metallurgy , thermodynamics , analytical chemistry (journal) , composite material , condensed matter physics , chemistry , ferromagnetism , physics , chromatography
Nickel ferrite (NiFe 2 O 4 ) is a major constituent of the corrosion deposits formed on the exterior of nuclear fuel cladding tubes during operation. NiFe 2 O 4 has attracted much recent interest, mainly due to the impact of these deposits, known as CRUD, on the operation of commercial nuclear reactors. Although advances have been made in modeling CRUD nucleation and growth under a wide range of conditions, the thermophysical properties of NiFe 2 O 4 at high temperatures have only been approximated, thereby limiting the accuracy of such models. In this study, samples of NiFe 2 O 4 were synthesized to provide the thermal diffusivity, specific heat capacity, and thermal expansion data from room temperature to 1300 K. These results were then used to determine thermal conductivity. Numerical fits are provided to facilitate ongoing modeling efforts. The Curie temperature determined through these measurements was in slight disagreement with literature values. Transmission electron microscopy investigation of multiple NiFe 2 O 4 samples revealed that minor nonstoichiometry was likely responsible for variations in the Curie temperature. However, these small changes in composition did not impact the thermal conductivity of NiFe 2 O 4 , and thus are not expected to play a large role in governing reactor performance.