Aqueous Gelcasting of Fused Silica Using Colloidal Silica Binder
Author(s) -
Manivannan R.,
Kumar Anil,
Subrahmanyam Ch.
Publication year - 2013
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/jace.12448
Subject(s) - materials science , colloidal silica , flexural strength , shrinkage , slurry , green body , composite material , sintering , colloid , rheology , aqueous solution , ceramic , precipitated silica , viscosity , chemical engineering , chemistry , coating , natural rubber , engineering
An aqueous‐based gelcasting of fused silica ceramics by using colloidal silica binder was developed. Fused silica slurries having different volume percentage of solid loading from 63 to 74 vol% in colloidal silica were made and the rheological properties were evaluated. It was found that the slurry with 73 vol% of solid loading with viscosity 0.70 Pa.s is suitable for this gelcasting system. The influence of solid loading on physical and mechanical properties of gelcast green and sintered bodies has been studied. The fabricated green body by using colloidal silica binder exhibited a flexural strength of 9 MPa and 88% of theoretical density with 2.2% of drying shrinkage while the sintered sample exhibited flexural strength of 60 MPa and 95% of theoretical density with 4.3% of sintering shrinkage. It was observed that, the nano silica particles from the colloidal silica binder is filling the interstitial positions in the consolidated fused silica green body and enhancing physical and mechanical properties.