Role of preliminary etching for one‐step self‐etch adhesives
Author(s) -
Taschner Michael,
Nato Fernando,
Mazzoni Annalisa,
Frankenberger Roland,
Krämer Norbert,
Di Lenarda Roberto,
Petschelt Anselm,
Breschi Lorenzo
Publication year - 2010
Publication title -
european journal of oral sciences
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.802
H-Index - 93
eISSN - 1600-0722
pISSN - 0909-8836
DOI - 10.1111/j.1600-0722.2010.00769.x
Subject(s) - materials science , adhesive , enamel paint , phosphoric acid , bond strength , etching (microfabrication) , composite material , dentistry , smear layer , layer (electronics) , scanning electron microscope , metallurgy , medicine
Taschner M, Nato F, Mazzoni A, Frankenberger R, Krämer N, Di Lenarda R, Petschelt A, Breschi L. Role of preliminary etching for one‐step self‐etch adhesives.
Eur J Oral Sci 2010; 118: 517–524. © 2010 Eur J Oral Sci The aim of this study was to analyse the effect of preliminary phosphoric acid etching of enamel and dentine before the application of two, one‐step self‐etch adhesive systems. The systems were applied onto acid‐etched or smear‐layer‐covered enamel and dentine. The treatment groups were as follows: group 1, Adper Easy Bond (3M ESPE) on etched substrate; group 2, Adper Easy Bond (control); group 3, iBond Self‐Etch (Heraeus Kulzer) on etched substrate; and group 4, iBond Self‐Etch (control). Enamel and dentine bond strengths were calculated using microshear and microtensile bond‐strength tests. Additional specimens were prepared to evaluate nanoleakage at the dentine–adhesive interface and were investigated using light microscopy or transmission electron microscopy. Both adhesives demonstrated higher microshear bond strengths when enamel was pre‐acid‐etched with phosphoric acid (Adper Easy Bond 28.7 ± 4.8 MPa; iBond Self‐Etch 19.7 ± 3.6 MPa) compared with controls (Adper Easy Bond 19.2 ± 3.3 MPa; iBond Self‐Etch 17.5 ± 2.7 MPa) and increased microtensile bond strength when applied on acid‐etched (Adper Easy Bond 35.8 ± 5.7 MPa; iBond Self‐Etch 24.3 ± 7.9 MPa) vs. smear‐layer‐covered dentine (Adper Easy Bond 26.9 ± 6.2 MPa; iBond Self‐Etch 17.6 ± 4.3 MPa). Adper Easy Bond showed lower nanoleakage than iBond Self‐Etch, irrespective of preliminary etching. The results of this study support the use of phosphoric acid etching before the application of one‐step self‐etch adhesive systems.