Stability and Microstructure of Indium Tin Oxynitride Thin Films
Author(s) -
Gregory Otto J.,
Amani Matin,
Tougas Ian M.,
Drehman Alvin J.
Publication year - 2012
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/j.1551-2916.2011.04845.x
Subject(s) - materials science , microstructure , sintering , crystallite , ceramic , indium , indium tin oxide , composite material , thin film , tin , oxide , layer (electronics) , metallurgy , nanotechnology
Indium oxide ( In 2 O 3 ) and indium tin oxide ( ITO ) thin films have been investigated for high temperature thermocouple and strain guage applications. Reactive sputtering in nitrogen‐rich plasmas was used to improve the high temperature stability of indium oxide‐based films in air and scanning electron microscopy was used to follow the microstructural changes in the nitrogen‐processed films. When thermally cycled at temperatures above 800°C, a partially sintered microstructure comprised of nanometer‐sized crystallites was revealed. A densified layer was also formed on the surface, which acted as an oxygen‐diffusion barrier in the bulk film. This combined with a network of partially sintered oxynitride crystallites lead to considerable open porosity and a stabilizing effect on the ensuing electrical properties. In this article, the thermoelectric properties of nitrogen‐processed films were evaluated at temperatures up to 1400°C. To study the effect of nitrogen plasma processing on the sintering kinetics and associated densification, the constrained sintering of the resulting films was followed as a function of time and temperature. Based on the measured thermoelectric properties of the nitrogen processed films, drift rates on the same order of magnitude as commercial type K wire thermocouples were realized for these all‐ceramic thermocouples.