Spin Spray‐Deposited Nickel Manganite Thermistor Films For Microbolometer Applications
Author(s) -
Ko Song Won,
Li Jing,
Podraza Nikolas J.,
Dickey Elizabeth C.,
TrolierMcKinstry Susan
Publication year - 2011
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/j.1551-2916.2010.04097.x
Subject(s) - manganite , materials science , nanocrystalline material , spinel , thin film , analytical chemistry (journal) , nickel , electrical resistivity and conductivity , annealing (glass) , mineralogy , nanotechnology , metallurgy , ferromagnetism , chemistry , condensed matter physics , physics , engineering , chromatography , electrical engineering
Nickel manganite thin films are good candidates for thermal imaging applications because of their large temperature coefficient of resistance (TCR), (>−3%/K) and good environmental stability. To enable low‐temperature deposition (90°C) on preexisting circuitry, a spin spray technique was developed for these materials. As‐deposited manganese oxide films show well‐developed X‐ray diffraction patterns, while as‐deposited nickel manganite films exhibit a nanocrystalline spinel structure. Low‐temperature (400°C) postdeposition annealing leads to densification of the nanocrystalline nickel manganite spinel films. Spectroscopic ellipsometry measurements on annealed films provide complex dielectric function spectra over a range from 0.75 to 5.15 eV with comparable features with those found in films prepared by a chemical solution method. Energy‐dispersive X‐ray spectroscopy indicates that the final composition of the films is Ni deficient relative to the starting solution composition. The TCR of the nickel manganite films annealed at 400°C in an argon atmosphere is −3.6%/K. Doping the nickel manganite films with zinc results in an improvement of crystallinity, but leads to substantial increases in the electrical resistivity. Copper doping reduces the resistivity of the films to <1.0 kΩ·cm without degrading the crystalline quality, thus resulting in films suitable for microbolometer applications.